Nanowires pave way for nanodevices
– from NC State News Services
Silicon nanowires are attracting significant attention from the electronics industry due to the drive for ever-smaller electronic devices, from cell phones to computers. The operation of these future devices, and a wide array of additional applications, will depend on the mechanical properties of these nanowires. New research from North Carolina State University shows that silicon nanowires are far more resilient than their larger counterparts, a finding that could pave the way for smaller, sturdier nanoelectronics, nanosensors, light-emitting diodes and other applications.
It is no surprise that the mechanical properties of silicon nanowires are different from “bulk” – or regular size – silicon materials, because as the diameter of the wires decrease, there is an increasing surface-to-volume ratio. Unfortunately, experimental results reported in the literature on the properties of silicon nanowires have reported conflicting results. So the NC State researchers set out to quantify the elastic and fracture properties of the material.
“The mainstream semiconductor industry is built on silicon,” says Dr. Yong Zhu, assistant professor of mechanical engineering at NC State and lead researcher on this project. “These wires are the building blocks for future nanoelectronics.” For this study, researchers set out to determine how much abuse these silicon nanowires can take. How do they deform – meaning how much can you stretch or warp the material before it breaks? And how much force can they withstand before they fracture or crack? The researchers focused on nanowires made using the vapor-liquid-solid synthesis process, which is a common way of producing silicon nanowires.
Zhu and his team measured the nanowire properties using in-situ tensile testing inside scanning electron microscopy. A nanomanipulator was used as the actuator and a micro cantilever used as the load sensor. “Our experimental method is direct but simple,” says Qingquan Qin, a Ph.D. student at NC State and co-author of the paper. “This method offers real-time observation of nanowire deformation and fracture, while simultaneously providing quantitative stress and strain data. The method is very efficient, so a large number of specimens can be tested within a reasonable period of time.”
As it turns out, silicon nanowires deform in a very different way from bulk silicon. “Bulk silicon is very brittle and has limited deformability, meaning that it cannot be stretched or warped very much without breaking.” says Feng Xu, a Ph.D. student at NC state and co-author of the paper, “But the silicon nanowires are more resilient, and can sustain much larger deformation. Other properties of silicon nanowires include increasing fracture strength and decreasing elastic modulus as the nanowire gets smaller and smaller.”
The fact that silicon nanowires have more deformability and strength is a big deal. “These properties are essential to the design and reliability of novel silicon nanodevices,” Zhu says. “The insights gained from this study not only advance fundamental understanding about size effects on mechanical properties of nanostructures, but also give designers more options in designing nanodevices ranging from nanosensors to nanoelectronics to nanostructured solar cells.”
The study, “Mechanical Properties of Vapor-Liquid-Solid Synthesized Silicon Nanowires,” was co-authored by Zhu, Xu, Qin, University of Michigan (UM) researcher Wei Lu and UM Ph.D. student Wayne Fung. The study is published in the Nov. 11 issue of Nano Letters, and was funded by grants from the National Science Foundation and NC State.
Media Contact:
Matt Shipman, News Services, 919.515.6386
Technical Contact:
Dr. Yong Zhu, 919.513.7735
Note to editors: The study abstract follows.
“Mechanical Properties of Vapor-Liquid-Solid Synthesized Silicon Nanowires”
Authors: Yong Zhu, Feng Xu, Qingquan Qin, North Carolina State University; Wayne F. Fung, Wei Lu, University of Michigan.
Published: November 11, 2009, Nano Letters
Abstract: The Young’s modulus and fracture strength of silicon nanowires with diameters between 15 and 60 nm and lengths between 1.5 and 4.3 micrometers were measured. The nanowires, grown by the vapor-liquid-solid process, were subjected to tensile tests in situ inside a scanning electron microscope. The Young’s modulus decreased while the fracture strength increased up to over 12 GPa, as the nanowire diameter decreased. The fracture strength also increased with the decrease of the side surface area; the increase rate for the chemically synthesized silicon nanowires was found to be much higher than that for the microfabricated silicon thin films. Repeated loading and unloading during tensile tests demonstrated that the nanowires are linear elastic until fracture without appreciable plasticity.
- Categories: